Structures by: Vasiliev A.
Total: 11
Rubidium nickel-iron borophosphate
B8FeH12Ni5O56P12,0.52(Rb2),2.96(Rb)
Dalton transactions (Cambridge, England : 2003) (2019) 48, 24 8835-8842
a=9.4599(4)Å b=12.2035(4)Å c=19.9085(6)Å
α=90° β=90° γ=90°
Caesium copper borophosphate
B8Cu6H12O56P12,4(Cs)
Dalton transactions (Cambridge, England : 2003) (2019) 48, 24 8835-8842
a=9.4057(5)Å b=12.9274(5)Å c=19.3912(9)Å
α=90° β=90° γ=90°
Caesium nickel borophosphate
B8H12Ni6O56P12,4(Cs)
Dalton transactions (Cambridge, England : 2003) (2019) 48, 24 8835-8842
a=9.5200(4)Å b=12.2546(5)Å c=19.9660(6)Å
α=90° β=90° γ=90°
Caesium borophosphate hydroxide
CsB1P2O6,2(OH)
Acta Crystallographica Section B (2019) 75, 6
a=13.4002(3)Å b=7.4869(2)Å c=14.5329(3)Å
α=90° β=90.059(2)° γ=90°
Caesium manganese borophosphate hydroxide
Cs,Mn,BO8P2,OH
Acta Crystallographica Section B (2019) 75, 6
a=9.1494(3)Å b=8.6991(2)Å c=9.6413(3)Å
α=90° β=100.141(2)° γ=90°
Caesium manganese borophosphate hydrate
Cs0.51Mn1.17,2(H2O),B1P2O8,0.45(H2O)
Acta Crystallographica Section B (2019) 75, 6
a=9.6292(3)Å b=9.6292(3)Å c=15.8051(5)Å
α=90° β=90° γ=120°
Potassium dimanganese trivanadate
KMn2O10V3
Acta Crystallographica Section B (2018) 74, 1 97-103
a=6.912(5)Å b=6.993(5)Å c=9.656(5)Å
α=101.858(5)° β=102.627(5)° γ=100.669(5)°
Dicesium copper tetraaluminate
Cs2CuAl4O8
Acta Crystallographica Section B (2015) 71, 5
a=8.4551(7)Å b=10.0120(10)Å c=17.073(2)Å
α=90° β=101.643(9)° γ=90°
AsFeLi
AsFeLi
Crystal Growth & Design (2010) 10, 10 4428
a=3.7678(4)Å b=3.7678(4)Å c=6.3151(8)Å
α=90.00° β=90.00° γ=90.00°
?
Bi10Fe6O38Ti7
Inorganic chemistry (2016) 55, 3 1245-1257
a=11.85114(17)Å b=3.85076(4)Å c=33.0722(6)Å
α=90° β=90° γ=90°
?
Bi10Fe6O38Ti7
Inorganic chemistry (2016) 55, 3 1245-1257
a=11.8510(2)Å b=3.85076(5)Å c=33.0704(7)Å
α=90° β=90° γ=90°